HIGH THERMAL SHOCK RESISTANCE • LOW THERMAL EXPANSION NON WETTING • LOW WEIGHT, HIGH DENSITY ALL OF THIS LEADING TO A LONGER LIFE OF THE TUBES IN MOLTEN METAL CONTACT APPLICATIONS NITRIDE BONDED CERAMICS SILICON CARBIDE HEATER PROTECTION TUBE FOR LPDC APPLICATIONS STALK TUBE FOR LPDC APPLICATION DOSING TUBE ASSEMBLY Maximum Hot Face Temperature Bulk Density Apparent Porosity Cold Crushing Strength Modulus of Rupture At Room Temperature At 1350 ̊ C Thermal Conductivity At 900 ̊ C Hot Face Temperature Chemical Analysis SiC Si 3 N 4 Others Fe 2 O 3 Recommended Laying Mortars 1550 2.63 min. 16.0 max. 1400 min. 300 min. 450 min. 15.3 80.0 min. 17.0 min. (Si 3 N 4 + Si 2 ON 2 ) - 0.5 max 1550 2.69 15.0 1600 325 500 15.0 81.0 18.0 min. (Si 3 N 4 + Si 2 ON 2 ) - 0.3 ̊ C gm/cc % Kg/cm 2 Kg/cm 2 W/m ̊ K % PROPERTIES UNIT SUPER Limit Value Typical Value 38, 17th Cross, Malleswaram, Bangalore - 560 055, India. Call +91 93414 43836 / 97411 65652 / +91 80 23347004 / 23462904 Email: info@silcarb.com | www.silcarb.com